High Performance Recessed Gate AlGaN/GaN HEMTs on Sapphire

Ilesanmi ADESIDA  Vipan KUMAR  Jinwei YANG  Muhammed Asif KHAN  

Publication
IEICE TRANSACTIONS on Electronics   Vol.E86-C   No.10   pp.1955-1959
Publication Date: 2003/10/01
Online ISSN: 
DOI: 
Print ISSN: 0916-8516
Type of Manuscript: INVITED PAPER (Special Issue on Heterostructure Microelectronics with TWHM2003)
Category: 
Keyword: 
GaN,  HEMTs,  sapphire,  

Full Text: PDF(658.1KB)>>
Buy this Article




Summary: 
Recessed 0.15 µm gate-length AlGaN/GaN high electron mobility transistors (HEMTs) were fabricated using inductively-coupled-plasma reactive ion etching (ICP-RIE) on sapphire substrate. These 0.15 µm gate-length devices exhibited maximum drain current density as high as 1.4 A/mm and peak extrinsic transconductance of 346 mS/mm. The threshold voltage was -4.1 V. A unity gain cut-off frequency (fT) of 80 GHz and maximum frequency of oscillation (fmax) of 73 GHz were measured on these devices. Pulsed I-(V) measurements did not show any significant dispersion. At 20 GHz, a continuous-wave (CW) output power density of 3.1 W/mm with power-added-efficiency (PAE) of 29.9% was obtained.